LNP™ THERMOCOMP™ RF004XXD compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oDU8Bw_LNP-THERMOCOMP-RF004XXD-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* RF004XXD is a compound based on Nylon 66 resin containing 20% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound RF-1004 Product reorder name: RF004XXD |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.30 | g/cm³ | ASTM D792 |
| -- | 1.29 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 1.2 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.47 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.80 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7170 | MPa | ASTM D638 |
| -- | 7300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 157 | MPa | ASTM D638 |
| Break | 160 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.6 | % | ASTM D638 |
| Break | 3.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5860 | MPa | ASTM D790 |
| -- | 7000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 231 | MPa | ASTM D790 |
| -- | 242 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.68 | ||
| vs. Itself - Static | 0.52 | ||
| Wear Factor - Washer | 80.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C 2 | 8.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 830 | J/m | ASTM D4812 |
| 23°C 3 | 56 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 11.4 | J | ASTM D3763 |
| -- | 2.49 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 260 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 247 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 221 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 3.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.9E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT PCR PA66 M40-300PCR | NEXT Specialty Resins, Inc. | Nylon 66 | NEXT PCR |
| Network Polymers PP PPH 30 1200 TF40 | Network Polymers, Inc. | PP Homopolymer | Network Polymers PP |
| Nitrovin™ 458 | Vi-Chem Corporation | TPV | Nitrovin™ |
| apigo® 9121/35 | API SpA | TPO (POE) | apigo® |
| TECHNYL® A 218HPS V50 BLACK 21N | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® RED |