Kepital® F10-03H
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oAQnMT_Kepital-F10-03H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A high viscosity grade for general injection molding with high stifness. It has improved on thermal stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| -- | 2.5 | g/10 min | ASTM D1238 |
| -- | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.00 mm | 2.0 | % | ASTM D955 |
| 3.00 mm | 2.2 | % | |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.22 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 64.0 | MPa | ASTM D638 |
| Yield, 23°C | 68.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 40 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 40 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2660 | MPa | ASTM D790 |
| 23°C | 2650 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 86.0 | MPa | ASTM D790 |
| 23°C | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Melting Temperature | 165 | °C | |
| CLTE - Flow (20 to 80°C) | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 19 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTFA 07 | Polymer Tailoring Ltd. | PP, Unspecified | PTFA |
| Resiten® 215FR | ITEN INDUSTRIES | Phenolic | Resiten® |
| DJSilicone NE-151 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| FERREX® GPP30CN36HB-GN | Ferro Corporation | PP, Unspecified | FERREX® |
| Lion Idemitsu Composites PPS Y531F1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |