Generic PPA
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oA0cOc_Generic-PPA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPA This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.10 - 1.39 | g/cm³ | ASTM D792 |
| 23°C | 1.10 - 1.26 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.063 - 2.0 | % | ASTM D955 |
| Transverse flow : 23°C | 0.10 - 2.1 | % | ASTM D955 |
| 23°C | 0.97 - 1.7 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.20 - 0.31 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2370 - 20900 | MPa | ASTM D638 |
| 23°C | 2100 - 15600 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield, 23°C | 61.7 - 79.4 | MPa | ISO 527-2 |
| Fracture, 23°C | 57.0 - 300 | MPa | ISO 527-2 |
| 23°C | 68.1 - 176 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.0 - 10 | % | ASTM D638 |
| Yield, 23°C | 2.0 - 6.5 | % | ISO 527-2 |
| Fracture, 23°C | 1.2 - 3.7 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 5.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2070 - 14200 | MPa | ASTM D790 |
| 23°C | 1790 - 10200 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 101 - 295 | MPa | ASTM D790 |
| 23°C | 70.3 - 285 | MPa | ISO 178 |
| Shear Strength (23°C) | 61.6 - 92.6 | MPa | ASTM D732 |
| Coefficient of Friction | 0.20 - 0.23 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 - 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 29 - 85 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 15 - 94 | J/m | ASTM D256 |
| 23°C | 2.7 - 75 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 80 - 1400 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C) | 1.36 - 54.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 130 - 301 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 101 - 146 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 100 - 132 | °C | ISO 75-2/A |
| Melting Temperature | 299 - 315 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+2 - 5.1E+15 | ohms·cm | ASTM D257 |
| 23°C | 7.5E+14 - 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 17 - 25 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 3.30 - 4.90 | ASTM D150 | |
| Dissipation Factor (23°C) | 9.0E-3 - 0.022 | ASTM D150 | |
| Comparative Tracking Index | 570 - 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 121 | °C | |
| Drying Time | 3.8 - 5.3 | hr | |
| Dew Point | -31.9 - -31.7 | °C | |
| Suggested Max Moisture | 0.045 - 0.15 | % | |
| Rear Temperature | 309 - 330 | °C | |
| Middle Temperature | 309 - 333 | °C | |
| Front Temperature | 309 - 338 | °C | |
| Processing (Melt) Temp | 315 - 331 | °C | |
| Mold Temperature | 78.0 - 160 | °C | |
| Injection Pressure | 96.3 - 98.7 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPAThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell PP EQ-14 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |
| Delta PC-1023 | Delta Polymers | PC | Delta |
| Karina IVORY PVC COMP. -E 801-35/ 1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| EPALINE 386A11 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPALINE |
| Sylvin 4200-88 Yellow 4192 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |