Plenco 01506 (Injection)
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o8RLyy_Plenco-01506-Injection-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 01506 is a mineral and cellulose filled granular polyester molding compound, with glass fiber reinforcement for improved mechanical strength properties. 01506 offers excellent electrical properties and resistance to chemical degradation from repeated detergent exposure. UL recognized under component file E40654. 01506 is available in beige. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Apparent Density | 0.70 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | ASTM D6289 | ||
| -- | 0.58 | % | ASTM D6289 |
| 120°C, 72 hours | 0.030 | % | ASTM D6289 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 61 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9560 | MPa | ASTM D638 |
| Tensile Strength | 52.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.1 | % | ASTM D638 |
| Flexural Modulus | 9330 | MPa | ASTM D790 |
| Flexural Strength | 95.0 | MPa | ASTM D790 |
| Compressive Strength | 131 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 25.3 | J/m | ASTM D256 |
| Notched Izod Impact | 30 | J/m | ASTM D256 |
| Drop Ball Impact | 204 | J/m | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 226 | °C | ASTM D648 |
| Continuous Use Temperature | 191 | °C | ASTM D794 |
| CLTE - Flow | 7.6E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.9E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 14 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.019 | ASTM D150 | |
| Arc Resistance | 190 | sec | ASTM D495 |
| Comparative Tracking Index | 600 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-1 | UL 94 | |
| Oxygen Index | 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Shot Size | 20 - 80 | % | |
| Rear Temperature | 49.0 - 71.0 | °C | |
| Front Temperature | 85.0 - 93.0 | °C | |
| Processing (Melt) Temp | 93.0 - 100 | °C | |
| Mold Temperature | 163 - 182 | °C | |
| Injection Pressure | 6.20 - 11.0 | MPa | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm | |
| Cushion | 3.00 | mm |
| Injection instructions |
|---|
| Injection Time: 3-6 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ BL-818.H001-8016 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Telcar® TELC-340 | Teknor Apex Company | TPE | Telcar® |
| Adiprene® LFP 1950A | Chemtura | PUR-Ester/PPDI | Adiprene® |
| Karina IVORY PVC COMPOUND 105905-35/ 1-BY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 2944-85 Clear 8413 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |