Udel® P-1710
| Category: | PSU , Polysulfone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Udel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o75WR0_Udel-P-1710.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Udel® P-1710 polysulfone (PSU) is a tough, rigid, high-strength thermoplastic that is suitable for continuous use up to 300°F (149°C). The resin is resistant to oxidation and hydrolysis and withstands prolonged exposure to high temperatures and repeated sterilization. Udel® P-1710 polysulfone is highly resistant to mineral acids, alkali and salt solutions. Its resistance to detergents and hydrocarbon oils is good, but it will be attacked by polar solvents such as ketones, chlorinated hydrocarbons and aromatic hydrocarbons. The resin is also highly resistant to degradation by gamma or electron beam radiation. Electrical properties are stable over a wide temperature range and after immersion in water or exposure to high humidity.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (343°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2480 | MPa | ASTM D638 |
| Tensile Strength | 70.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 to 100 | % | ASTM D638 |
| Flexural Modulus | 2690 | MPa | ASTM D790 |
| Flexural Strength | 106 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Tensile Impact Strength | 420 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 174 | °C | ASTM D648 |
| CLTE - Flow | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.15 | ||
| 1 kHz | 3.14 | ||
| 1 MHz | 3.10 | ||
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 1.1E-3 | ||
| 1 kHz | 1.3E-3 | ||
| 1 MHz | 5.0E-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 to 163 | °C | |
| Drying Time | 3.5 | hr | |
| Suggested Shot Size | 50 to 75 | % | |
| Processing (Melt) Temp | 329 to 385 | °C | |
| Mold Temperature | 121 to 163 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8984-78 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen EP348N | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Daelim Po1y® LL-34H | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| Huafon JF-HSY-AD | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| LARIPUR® LPR 5725 | COIM S.p.A. | TPU-Polyester | LARIPUR® |