LNP™ STAT-LOY™ A3000 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o6dgPL_LNP-STAT-LOY-A3000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY* A3000 is a compound based on ABS resin. Added feature of this material is: Antistatic. Also known as: LNP* STAT-LOY* Compound A Product reorder name: A3000 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 | g/cm³ | ASTM D792 |
| -- | 1.06 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.49 | % | ISO 294-4 |
| Flow : 24 hr | 0.41 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 1.1 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2010 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 39.1 | MPa | ASTM D638 |
| Yield | 38.0 | MPa | ISO 527-2 |
| Break | 36.7 | MPa | ASTM D638 |
| Break | 31.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.1 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2 |
| Break | 6.0 | % | ASTM D638 |
| Break | 24 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2100 | MPa | ASTM D790 |
| -- | 1980 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 65.7 | MPa | ASTM D790 |
| -- | 59.1 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 280 | J/m | ASTM D256 |
| 23°C 2 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 32.8 | J | ASTM D3763 |
| -- | 26.9 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 88.9 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 3 | 91.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 76.7 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 76.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 9.3E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 to 1.0E+11 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Processing (Melt) Temp | 199 to 210 | °C | |
| Mold Temperature | 10.0 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Megatron® 100L-MOS2 | Mega Polymers | Nylon 66 | Megatron® |
| Thermylene® P6-30FM-Y249B | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Zytel® FR70M30V0 BK010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| DuPont™ 20 Series DPE-2020T | DuPont Packaging & Industrial Polymers | LDPE | DuPont™ 20 Series |
| POCAN® B 3215 XF 000000 | LANXESS Asia/Pacific | PBT | POCAN® |