G-PAEK™ 1100ESG
| Category: | PEK , Polyether Ketone |
| Manufacturer: | Gharda Chemicals Ltd. |
| Trademark: | G-PAEK™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o6agWo_G-PAEK-1100ESG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Details: Ultra high Performance thermoplastic polymer, virgin, semicrystalline granules suitable for stock shapes extrusion, easy flow, Beige in color. Application Areas: Suitable for high temperature applications, high wear & abrasion resistance, and high chemical resistance is required & for metal replacement with plastics etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | |
| Molding Shrinkage 1 | |||
| Flow | 1.0 | % | |
| Across Flow | 1.3 | % | |
| Water Absorption (Equilibrium) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 100 | ASTM D785 | |
| Durometer Hardness (Shore D) | 86 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4200 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 20 to 25 | % | ASTM D638 |
| Flexural Modulus (23°C) | 4100 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 185 | MPa | ASTM D790 |
| Compressive Strength | 135 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 175 | °C | ASTM D648 |
| Continuous Use Temperature | 280 | °C | UL 746B |
| Glass Transition Temperature | 152 | °C | ASTM D3418 |
| Melting Temperature | 372 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C, 1000 sec^-1) | 300 to 350 | Pa·s | ASTM D3835 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Adapter Temperature | 400 | °C | |
| Melt Temperature | 390 to 400 | °C |
| Note Message | |
|---|---|
| 1 . | 400°C nozzle, 210°C Mold |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIC3704 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| NEFTEKHIM PP 8348U (EPL31UA) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Ferro PP LPP40BK49BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Formolene® 3355E | Formosa Plastics Corporation, U.S.A. | PP Random Copolymer | Formolene® |
| Elastollan® 688A10N Film | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyester | Elastollan® |