LNP™ KONDUIT™ DTK22 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ KONDUIT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o6VetM_LNP-KONDUIT-DTK22-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermally conductive, high impact, mineral filled PC composition Also known as: LNP* KONDUIT* Compound DTK22 Product reorder name: DTK22 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.41 | % | |
| Across Flow : 24 hr | 0.39 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3830 | MPa | ASTM D638 |
| -- | 3880 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 41.0 | MPa | ASTM D638 |
| Break | 42.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 5.0 | % | ASTM D638 |
| Break | 4.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 3160 | MPa | ASTM D790 |
| -- 5 | 4180 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 81.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 79.0 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 77.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 700 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 127 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 128 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 6.40 mm | 121 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 119 | °C | ISO 75-2/Af |
| Thermal Conductivity | |||
| -- 10 | 0.60 | W/m/K | ASTM E1461 |
| -- 11 | 2.0 | W/m/K | ASTM E1461 |
| -- 12 | 0.30 | W/m/K | ISO 22007-2 |
| -- 13 | 1.3 | W/m/K | ISO 22007-2 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.10 GHz) | 3.66 | ASTM ES7-83 | |
| Dissipation Factor (1.10 GHz) | 9.4E-3 | ASTM ES7-83 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 260 to 282 | °C | |
| Front Temperature | 271 to 293 | °C | |
| Nozzle Temperature | 266 to 288 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| 10 . | through-plane, 10*10*3mm sample |
| 11 . | in-plane, ø25*0.4mm disc |
| 12 . | through-plane, 60*60*3mm plaque |
| 13 . | in-plane, 60*60*3mm plaque |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GF 30 HE | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| XANTAR® G4F 22 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Bynel® 41E556 | DuPont Packaging & Industrial Polymers | LLDPE | Bynel® |
| Grilamid® XE 3997 nat | EMS-GRIVORY | Nylon 12 | Grilamid® |
| 3M™ Dyneon™ Fluoroelastomer FE 5610N | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |