DIC.PPS SE-730
| Category: | PPS+PPE , Polyphenylene Sulfide + PPE |
| Manufacturer: | DIC Corporation |
| Trademark: | DIC.PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o6K2gF_DIC-PPS-SE-730.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | |
| Across Flow | 1.0 | % | |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 100 | ||
| R-Scale | 121 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ASTM D638 |
| Tensile Strength | 150 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 10000 | MPa | ASTM D790 |
| Flexural Strength | 220 | MPa | ASTM D790 |
| Compressive Strength | 170 | MPa | ASTM D695 |
| Poisson's Ratio | 0.36 | ||
| Coefficient of Friction 1 | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.35 | ||
| vs. Steel - Static | 0.36 | ||
| Flexural Elongation at Break | 2.7 | % | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact | 650 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 255 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 90°C | 2.4E-5 | cm/cm/°C | |
| Transverse : -30 to 90°C | 2.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-3 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 300 to 330 | °C | |
| Middle Temperature | 300 to 330 | °C | |
| Front Temperature | 300 to 330 | °C | |
| Mold Temperature | 120 to 150 | °C |
| Note Message | |
|---|---|
| 1 . | P=150KPa, V=0.3m/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTAL PM1509 | Polyram Ram-On Industries | Acetal (POM) Copolymer | RAMTAL |
| YUNCON® N350 | YunNan YunTianHua Co., Ltd. | Acetal (POM) Copolymer | YUNCON® |
| LG PMMA IF860 | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| Petlon Prime B1-00-00-BK | Petlon Polymers Ltd | Nylon 6 | Petlon Prime |
| TechnoElast S A7002 I 1 nat | TechnoCompound GmbH | TPE | TechnoElast |