LubriOne™ PC-10GF/15T BLACK
| Category: | PC , Polycarbonate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o5oQR9_LubriOne-PC-10GF-15T-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PTFE lubricated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 72.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 3500 | MPa | ASTM D790 |
| Flexural Strength 3 | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 135 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 290 - 310 | °C | |
| Middle Temperature | 290 - 310 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Mold Temperature | 90.0 - 110 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LXR510H | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| NILENE® P K20T | Taro Plast S.p.A. | PP Homopolymer | NILENE® |
| AKROMID® B3 GF 40 S1 black (3384) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Bergamid™ A700 G25 H (f1) | PolyOne Corporation | Nylon 66 | Bergamid™ |
| ISORENE™ CA3-7001 | SABIC Innovative Plastics Europe | TPE | ISORENE™ |