TOTAL Polyethylene HDPE HL 428
| Category: | HDPE, MMW , High Density (MMW) Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o5IlEt_TOTAL-Polyethylene-HDPE-HL-428.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polyethylene HL 428 is a High Density (MMW) Polyethylene material. It is available in North America for coextrusion. Important attributes of TOTAL Polyethylene HL 428 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.947 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.28 | g/10 min | |
| 190°C/21.6 kg | 20 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus 1 | ASTM D882A | ||
| 1% Secant, MD : 25 µm, Blown Film | 710 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 1000 | MPa | |
| Tensile Strength | ASTM D882A | ||
| MD : Yield, 25 µm, Blown Film 2 | 24.1 | MPa | |
| MD : Yield, 25 µm, Blown Film 3 | 23.4 | MPa | |
| TD : Yield, 25 µm, Blown Film 4 | 25.5 | MPa | |
| TD : Yield, 25 µm, Blown Film 5 | 26.2 | MPa | |
| MD : Break, 25 µm, Blown Film 6 | 54.5 | MPa | |
| MD : Break, 25 µm, Blown Film 7 | 62.1 | MPa | |
| TD : Break, 25 µm, Blown Film 8 | 39.3 | MPa | |
| TD : Break, 25 µm, Blown Film 9 | 18.6 | MPa | |
| Tensile Elongation | ASTM D882A | ||
| MD : Break, 25 µm, Blown Film 10 | 600 | % | |
| MD : Break, 25 µm, Blown Film 11 | 450 | % | |
| TD : Break, 25 µm, Blown Film 12 | 700 | % | |
| TD : Break, 25 µm, Blown Film 13 | 600 | % | |
| Dart Drop Impact | ASTM D1709A | ||
| 25 µm, Blown Film 14 | 100 | g | |
| 25 µm, Blown Film 15 | < 50 | g | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film 16 | 28 | g | |
| MD : 25 µm, Blown Film 17 | 10 | g | |
| TD : 25 µm, Blown Film 18 | 530 | g | |
| TD : 25 µm, Blown Film 19 | 1500 | g | |
| Water Vapor Transmission Rate | ASTM F1249 | ||
| 25 µm 20 | 11 | g/m²/24 hr | |
| 25 µm, Blown Film 21 | 7.8 | g/m²/24 hr |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 131 | °C | ASTM D3417 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 to 216 | °C |
| Note Message | |
|---|---|
| 1 . | 2.5 BUR |
| 2 . | High Stalk, 6:1 FLH/D, 4:1 BUR |
| 3 . | 2.5 BUR |
| 4 . | High Stalk, 6:1 FLH/D, 4:1 BUR |
| 5 . | 2.5 BUR |
| 6 . | High Stalk, 6:1 FLH/D, 4:1 BUR |
| 7 . | 2.5 BUR |
| 8 . | High Stalk, 6:1 FLH/D, 4:1 BUR |
| 9 . | 2.5 BUR |
| 10 . | High Stalk, 6:1 FLH/D, 4:1 BUR |
| 11 . | 2.5 BUR |
| 12 . | High Stalk, 6:1 FLH/D, 4:1 BUR |
| 13 . | 2.5 BUR |
| 14 . | High Stalk, 6:1 FLH/D, 4:1 BUR |
| 15 . | 2.5 BUR |
| 16 . | High Stalk, 6:1 FLH/D, 4:1 BUR |
| 17 . | 2.5 BUR |
| 18 . | High Stalk, 6:1 FLH/D, 4:1 BUR |
| 19 . | 2.5 BUR |
| 20 . | 2.5 BUR |
| 21 . | High Stalk, 6:1 FLH/D, 4:1 BUR |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYplex PMMA 500 | Polykemi AB | Acrylic (PMMA) | POLYplex |
| Regis® 6015 | Noble Polymers | Polyolefin, Unspecified | Regis® |
| TPC PVC SM84E | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| Geon™ Vinyl Rigid Molding M3850 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| LNP™ THERMOCOMP™ JF006 compound | SABIC Innovative Plastics Europe | PESU | LNP™ THERMOCOMP™ |