LNP™ LUBRICOMP™ 9X06030 compound
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o5GhuB_LNP-LUBRICOMP-9X06030-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* 9X06030 is a compound based on PA46 resin containing PTFE and Carbon Fiber. Added features include: Internally Lubricated, Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound STN-CL-4016 HS Product reorder name: 9X06030 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.20 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 25700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 260 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 19100 | MPa | ISO 178 |
| Flexural Stress | 359 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 2.5 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 7.6E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 299 to 310 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 310 to 321 | °C | |
| Mold Temperature | 82.2 to 121 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE CC3054 | Saudi Basic Industries Corporation (SABIC) | HDPE Copolymer | SABIC® HDPE |
| Tectron H2409 | TECTRON Systems Pte Ltd | TPV | Tectron |
| NORYL GTX™ GTX679 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| DIOSHY® LP-855 | DIOSHY Co.,Ltd. | SEBS+SBS | DIOSHY® |
| Plexiglas® V920-UVT | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |