Ebalta MG 321 FR-S / Comp. A+B

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	Ebalta Kunststoff GmbH
Trademark:	Ebalta
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	o4UIkP_Ebalta-MG-321-FR-S-Comp-A-B.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ebalta MG 321 FR-S is processed on a two-component low pressure device.

After grinding with a sand paper , grit 280, the surface can be varnished with a commercial lacquer. For better adhesion we recommend the use of a primer coat. Nitrocellulose lacquers have a better adhesion on polyurethane surfaces than on acryl-lacquer-systems.

Applications

Cladding parts EDP field

Cladding parts medical sector

Interior / Exterior of rail vehicle

Properties

self-extinguishing according to UL 94 V0-FileE191776, Vol. 1

self-extinguishing according to UL 94 5 VA, File E191776, Vol. 1

Classification DIN 5510-2

precautionary fire protection in rail vehicles

for 4 mm wall thickness: S-3; SR1; ST2

high heat resistance

big wall thickness possible

General Information
Features	High Heat Resistance Self Extinguishing
Appearance	Natural Color
Processing Method	Casting

Hardness	Nominal Value		Test Method
Shore Hardness (Shore D)	77 to 83		ISO 7619

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus	1900 to 2100	MPa	ISO 178
Flexural Stress	59.0 to 69.0	MPa	ISO 178
Compressive Stress	63.0 to 73.0	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength	19 to 23	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	117 to 123	°C	ISO 75-2/B
Glass Transition Temperature	130 to 136	°C	DMA

Flammability	Nominal Value		Test Method
Flame Rating			UL 94
3.00 mm	V-0 5VA
4.00 mm	5VA

Thermoset	Nominal Value	Unit
Thermoset Components
Hardener	Mix Ratio by Volume: 51 Mix Ratio by Weight: 50
Resin	Mix Ratio by Weight: 100 Mix Ratio by Volume: 100
Post Cure Time
80°C	4.0	hr
120°C	2.0	hr

Uncured Properties	Nominal Value	Unit
Density (20°C)	1.20 to 1.26	g/cm³
Viscosity (25°C)	1.5 to 2.5	Pa·s
Curing Time (50°C)	0.25 to 0.33	hr
Pot Life (20°C)	0.83 to 1.0	min

Resin Grade	Manufacturer	Category	Trademark
Mirakutoran® TPU E785PSDH	Japan Mirakutoran Inc.	TPU Alloy	Mirakutoran® TPU
RTP 104 HB	RTP Company	PP, Unspecified	RTP
UBE Nylon PAE1201U	UBE America, Inc.	Nylon 12 Elast	UBE Nylon
InnoPlus LL8420A	PTT Global Chemical Public Company Limited	LLDPE	InnoPlus
Pebax® 7033 SA 01	Arkema	PEBA-Ether	Pebax®