Capran Medallion庐 MT-2500
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Honeywell |
| Trademark: | Capran Medallion® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o4UCv0_Capran-Medallion-MT-2500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CAPRAN MEDALLION® MT2500 is a 1.00 mil (25 micron) biaxially oriented nylon 6 film with a metallized barrier coating well suited for high barrier packaging applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.18 | ASTM D1894 | |
| With self-dynamics | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 25 µm | 3100 | MPa | ASTM D882 |
| TD : 25 µm | 2550 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 25 µm | 276 | MPa | ASTM D882 |
| TD : Break, 25 µm | 345 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 100 | % | ASTM D882 |
| TD : Break, 25 µm | 80 | % | ASTM D882 |
| Oxygen Permeability (23°C, 25 µm) | 0.028 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (25 µm, 38°C, 100% RH) | 2.6 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Additional Information |
|---|
| Yield: 23964 in²/lbTensile Strength @ Break, ASTM D 882, MD: 35000 to 45000 psiTensile Strength @ Break, ASTM D 882, TD: 45000 to 55000 psiElongation @ Break, ASTM 882, MD: 90 to 110%Elongation @ Break, ASTM 882, TD: 70 to 90%Secant Modulus, ASTM D 882, MD: 400000 to 500000 psiSecant Modulus, ASTM D 882, TD: 320000 to 420000 psiGraves Tear (initial), ASTM D 1004, MD: 1000 to1400 g/milGraves Tear (initial), ASTM D 1004, TD: 1000 to1500 g/milCoefficient of Friction, ASTM D 1894: 0.40 to 0.60 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.13 to 0.24 vs Metal-DynamicHelium Transmission Rate, ASTM D 1434, 73°F/0%RH: <6 cc/100in²/daySurface Tension, ASTM D5946, untreated side: 48 to 50 dynes/cmDimensional Stability, ASTM D1204, MD, 320°F, 5min: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: 1.0 to 2.0% shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polyvel PLA CT-L03 PLA Melt Strength Enhancer (FDA) | Polyvel Inc. | PLA | Polyvel PLA |
| Network Polymers Polyester 60 3301 | Network Polymers, Inc. | Polyester, TP | Network Polymers Polyester |
| BCC Resins BC 5009 | BCC Products Inc. | Epoxy | BCC Resins |
| Lionpol LC-60060 | Lion Polymers Incorporated | TPE | Lionpol |
| Rotuba CAB B900 (20% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |