Hanwha Total PP BB150
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o4R1zE_Hanwha-Total-PP-BB150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BB150 is an impact polypropylene for injection molding applications. The polymerization technology and optimum rubber design offer an excellent balance between stiffness and impact strength. Characteristics and Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 29.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 500 | % | ASTM D638 |
| Flexural Modulus | 1180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 49 | J/m | |
| 0°C | 88 | J/m | |
| 23°C | 590 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 107 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-8162 | Ravago Manufacturing Americas, LLC | PP Homopolymer | Ravago Compounds |
| Shinite® PBT D202 | Shinkong Synthetic Fiber Corp. | PBT | Shinite® PBT |
| TYRIN™ 6000 | The Dow Chemical Company | CPE | TYRIN™ |
| Edistir® RC 600 | Versalis S.p.A. | PS (MIPS) | Edistir® |
| Latigray 37 B01-01 CX/35 | LATI S.p.A. | PLA | Latigray |