Iupilon® CLS1000
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o3gag4_Iupilon-CLS1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupilon®CLS1000 is a polycarbonate (PC) material,. This product is available in North America, Europe or Asia Pacific region. The processing method is injection molding. Iupilon®The main features of the CLS1000 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.3 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Vertical flow direction : 3.20mm | 0.50 - 0.70 | % | |
| Flow direction : 3.20mm | 0.50 - 0.70 | % | |
| Water Absorption (Saturation, 23°C) | 0.24 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.4 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 110 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 88 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 145 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 131 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 1.00 mm | 31 | kV/mm | IEC 60243-1 |
| 3.00 mm | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.10 | IEC 60250 | |
| 1 MHz | 3.10 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 6.0E-4 | IEC 60250 | |
| 1 MHz | 9.0E-3 | IEC 60250 |
| Additional Information |
|---|
| Cut UV of under 380nm at 3mmt |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 270 - 300 | °C | |
| Nozzle Temperature | 270 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2903-60 White 148 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vi-Chem PVC VNC50D-30I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Diakon® Frost 902 80 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| DuraStar™ MN630 | Eastman Chemical Company | Polyester, TP | DuraStar™ |
| Elastollan® 1195A55 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |