AVP™ KLL10FR
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | AVP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o2xH1i_AVP-KLL10FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AVP™ KLL10FR is a Polycarbonate (PC) product filled with 10% glass fiber. It can be processed by injection molding and is available in North America. Applications of AVP™ KLL10FR include electrical/electronic applications, appliances and automotive. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength 1(Yield, 3.18 mm) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.18 mm) | 15 | % | ASTM D638 |
| Flexural Modulus 3(3.18 mm, 50.8 mm Span) | 3170 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.18 mm, 50.8 mm Span) | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 138 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.10 mm | V-0 | ||
| 3.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 6.0 | hr | |
| Drying Time, Maximum | 16 | hr | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 316 | °C | |
| Front Temperature | 288 to 316 | °C | |
| Nozzle Temperature | 288 to 316 | °C | |
| Processing (Melt) Temp | 304 to 332 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 1.38 | MPa |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPPLEN® H 649 FH | MOL Petrochemicals Co. Ltd. | PP Homopolymer | TIPPLEN® |
| Ethavin™ C85FRNC | Vi-Chem Corporation | TPO (POE) | Ethavin™ |
| DEXFLEX® D60-UV | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| DOWLEX™ 5075G | The Dow Chemical Company | LLDPE | DOWLEX™ |
| Hylon® N1240MG25L | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |