Stat-Tech™ PC-CB2/000 CR XP100827 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 to 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2070 to 3450 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 55.2 to 72.4 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.0 to 7.0 | % | ASTM D638 |
| Flexural Modulus | 1720 to 3100 | MPa | ASTM D790 |
| Flexural Strength | 89.6 to 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm, Injection Molded) | 37 to 53 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 123 | °C | |
| 1.8 MPa, Unannealed | 112 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 to 1.0E+4 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 300 to 320 | °C | |
| Mold Temperature | 90.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3896 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Quadrant EPP CESTILENE HD 1000 | Quadrant Engineering Plastic Products | UHMWPE | Quadrant EPP |
| Cyclics® C99 | Cyclics Corporation | PBT | Cyclics® |
| JSR EPR EP503EF | JSR Corporation | EPDM | JSR EPR |
| LOXIM 830 02C HB | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |