Ryton® R-4-220NA
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Ryton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o2nvpM_Ryton-R-4-220NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ryton® R-4-220NA and R-4-220BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength after constant or repeated exposure to high temperature water. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.20 | % | |
| Across Flow : 3.20 mm | 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 103 | ||
| R-Scale | 122 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 186 | MPa | ASTM D638 |
| -- | 190 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 1.6 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 14500 | MPa | ASTM D790 |
| -- | 14000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 269 | MPa | ASTM D790 |
| -- | 275 | MPa | ISO 178 |
| Compressive Strength | 275 | MPa | ASTM D695 |
| Poisson's Ratio | 0.37 | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 3.18 mm | 91 | J/m | ASTM D256 |
| -- | 9.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact | |||
| 3.18 mm | 640 | J/m | ASTM D4812 |
| -- | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -50 to 50°C | 1.5E-5 | cm/cm/°C | |
| Flow : 100 to 200°C | 1.5E-5 | cm/cm/°C | |
| Transverse : -50 to 50°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 100 to 200°C | 8.5E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.31 | W/m/K | |
| UL Temperature Rating | 200 to 220 | °C | UL 746B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 25°C, 1 kHz | 3.80 | ||
| 25°C, 1 MHz | 3.80 | ||
| Dissipation Factor | ASTM D150 | ||
| 25°C, 1 kHz | 2.0E-3 | ||
| 25°C, 1 MHz | 3.0E-3 | ||
| Arc Resistance | 125 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 150 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Oxygen Index | 45 | % | ASTM D2863 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Hydrolytic Stability 1 | |||
| Tensile Strength Retained | > 80 | % | |
| Weight Gain | < 1.0 | % |
| Note Message | |
|---|---|
| 1 . | Test specimens aged 1000 hours in water at 140°C (284°F) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ReoFlex® 50 | Smooth-On, Inc | PUR, Unspecified | ReoFlex® |
| Weatherflex™ CS1521WX NTL01B | Colorite Polymers | PVC, Flexible | Weatherflex™ |
| Ultramid® B3Z BK30464 | BASF Corporation | Nylon 6 | Ultramid® |
| Cadence™ GS2 | Eastman Chemical Company | Copolyester | Cadence™ |
| HI-ZEX™ 540E | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |