Ipethene® 4203
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Ipethene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o2PDmf_Ipethene-4203.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IPETHENE® 4203 is a low density polyethylene extrusion grade, produced by high pressure autoclave technology. It exhibits high mechanical strength, good Environmental Stress Cracking Resistance (ESCR) and very good bubble stability even in large diameter blown film processing. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.20 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 100 µm, blown film | 23.0 | MPa | ISO 527-3 |
| TD : Broken, 100 µm, blown film | 26.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 100 µm, blown film | 650 | % | ISO 527-3 |
| TD : Broken, 100 µm, blown film | 700 | % | ISO 527-3 |
| Dart Drop Impact 1(100 µm, Blown Film) | 500 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 100 µm, blown film | 0.025 | N | ISO 6383-2 |
| TD : 100 µm, blown film | 0.046 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ISO 306 |
| Melting Temperature 2 | 109 | °C | ISO 11357-3 |
| Additional Information |
|---|
| Film properties: Measured on 100 µm blown film, Blow-up ratio 2.5:1, output 10 kg/h, melt temperature ~210°C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | By DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR Z9450 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Viton® B-70 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| NEFTEKHIM PP 4348S | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Hypro® PPH-CC10 NATURAL | Entec Polymers | PP Homopolymer | Hypro® |
| TechnoFiber Performance PP LGF 20-10-02 HI | TechnoCompound GmbH | PP, Unspecified | TechnoFiber Performance |