NORYL GTX™ GTX4610 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o2GFmq_NORYLGTXGTX4610resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL GTX GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, strength, and flow. The material is available in limited colors for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 18 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.88 - 0.94 | % | Internal method |
| Transverse flow : 3.20mm | 0.95 - 1.0 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 3.8 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5000 | MPa | ASTM D638 |
| -- | 5000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 88.0 | MPa | ASTM D638 |
| Yield | 88.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 88.0 | MPa | ASTM D638 |
| Fracture | 88.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Fracture 5 | 7.0 | % | ASTM D638 |
| Fracture | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 4600 | MPa | ASTM D790 |
| -- 7 | 4600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 145 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 65 | J/m | ASTM D256 |
| 23°C | 80 | J/m | ASTM D256 |
| -30°C 10 | 5.5 | kJ/m² | ISO 180/1A |
| 23°C 11 | 7.0 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 12.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 220 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 12 | 224 | °C | ISO 75-2/Bf |
| Vicat Softening Temperature | |||
| -- | 218 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 220 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 7.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Air | 23 | kV/mm | ASTM D149 |
| 1.60 mm, in Oil | 24 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| Comparative Tracking Index | 425 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm, Testing by SABIC | V-1 | UL 94 | |
| 2.00 mm, Testing by SABIC | 5VB 5VA | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 825 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 - 107 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Suggested Shot Size | 30 - 50 | % | |
| Rear Temperature | 266 - 304 | °C | |
| Middle Temperature | 271 - 304 | °C | |
| Front Temperature | 277 - 304 | °C | |
| Nozzle Temperature | 282 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 76.7 - 121 | °C | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.038 | mm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02 % |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STARLEX E/8025-86 naturale | Daloga srl | TPU-Polyether | STARLEX |
| Surlyn® 8940-E | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| Formolon® 685 | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| LNP™ STAT-KON™ DX95523C compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| ALTECH® PA66 ECO 2033/509 GF33 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |