DIAMALOY ENGINEERED ALLOYS PCPBT 530
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | DIAMALOY ENGINEERED ALLOYS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o2AqRR_DIAMALOY-ENGINEERED-ALLOYS-PCPBT-530.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DIAMALOY ENGINEERED ALLOYS PCPBT 530 is a Polycarbonate + PBT (PC+PBT) product. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(265°C/5.0 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 62.1 | MPa | ASTM D638 |
| Flexural Modulus 3 | 2450 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 750 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 102 | °C | ASTM D648 |
| Vicat Softening Temperature | 133 | °C | ASTM D1525 4 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 104 to 110 | °C | |
| Drying Time - Desiccant Dryer | 4.0 to 6.0 | hr | |
| Dew Point - Desiccant Dryer | < -28.9 | °C | |
| Suggested Shot Size | 60 to 80 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 243 to 266 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 260 to 282 | °C | |
| Nozzle Temperature | 260 to 288 | °C | |
| Processing (Melt) Temp | 260 to 288 | °C | |
| Mold Temperature | 54.4 to 82.2 | °C | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 0.345 to 0.517 | MPa | |
| Back Pressure | 0.552 to 1.03 | MPa | |
| Screw Speed | 50 to 75 | rpm | |
| Clamp Tonnage | 4.1 to 6.9 | kN/cm² | |
| Cushion | 2.54 to 7.62 | mm |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Method I (3 point load), 1.3 mm/min |
| 4 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titalon® 3315TF | Titan Plastics Compounds Co., Ltd. | Nylon 12 | Titalon® |
| Ultraform® N 2320 U03 UNC Q600 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Chemlon® 133 GHR | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| LNP™ STAT-KON™ AX02747 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-KON™ |
| Infino TK-2050HL | LOTTE ADVANCED MATERIALS CO., LTD. | PCT | Infino |