XENOY™ X5100 resin
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o29Ueq_XENOY-X5100-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XENOY X5100 is a semi-crystalline, impact modified PC-PBT blend with excellent flow. (PC+PBT-I). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.70 to 1.0 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2150 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 54.0 | MPa | |
| Break | 40.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 4.5 | % | |
| Break | 50 | % | |
| Flexural Modulus 2 | 2050 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 3 | 15 | kJ/m² | |
| 0°C 4 | 40 | kJ/m² | |
| 23°C 5 | 50 | kJ/m² | |
| Charpy Unnotched Impact Strength 6(-30°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength 7 | ISO 180/1A | ||
| -30°C | 18 | kJ/m² | |
| -20°C | 20 | kJ/m² | |
| -10°C | 35 | kJ/m² | |
| 0°C | 40 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 105 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 84.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ISO 306/A50 |
| -- | 117 | °C | ISO 306/B50 |
| -- | 120 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 8.5E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 215 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 240 to 265 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 255 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*3 sp=62mm |
| 5 . | 80*10*4 sp=62mm |
| 6 . | 80*10*4 sp=62mm |
| 7 . | 80*10*4 |
| 8 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVALAC RX®866 | Vyncolit N.V. | Phenolic | NOVALAC |
| Baydur® STR/C-1000 (38% Glass) | Covestro - PUR | PUR-MDI | Baydur® |
| ANYPOL SE-2500 | SH Energy & Chemical | PS (EPS) | ANYPOL |
| Escorene™ Ultra UL 15028CC | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Hanwha Total PE 530G | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LDPE | Hanwha Total PE |