KetaSpire® KT-820 GF30
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | KetaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o0eAdX_KetaSpire-KT-820-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KetaSpire® KT-820 GF30 is a medium flow, 30% glass fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire® PEEK resin. Reinforcement also affords greater mechanical robustness in structural applications, particularly those with service temperatures approaching 300°C. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of best-in-class fatigue resistance, ease of melt processing, high purity, and excellent chemical resistance to organics, acids, and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing, and other industrial uses. Beige: KetaSpire® KT-820 GF30 BG20 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow : 3.18 mm | 0.20 to 0.40 | % | |
| Across Flow : 3.18 mm | 1.4 to 1.6 | % | |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 100 | ASTM D785 | |
| Durometer Hardness (Shore D, 1 sec) | 91 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 10500 | MPa | ASTM D638 |
| -- | 11400 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 3 | 158 | MPa | ASTM D638 |
| Yield | 165 | MPa | ISO 527-2/1A/5 |
| -- | 158 | MPa | ASTM D638 |
| Nominal Tensile Strain at Break | |||
| -- 4 | 2.7 | % | ASTM D638 |
| -- | 2.7 | % | ISO 527-2/1A/5 |
| Flexural Modulus | |||
| -- | 10300 | MPa | ASTM D790 |
| -- | 10700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 271 | MPa | ASTM D790 |
| -- | 246 | MPa | ISO 178 |
| Yield | 261 | MPa | ASTM D790 |
| Compressive Strength | 169 | MPa | ASTM D695 |
| Shear Strength | 93.1 | MPa | ASTM D732 |
| Poisson's Ratio | 0.34 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 110 | J/m | ASTM D256 |
| -- | 13 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| -- | 960 | J/m | ASTM D4812 |
| -- | 56 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 315 | °C | ASTM D648 |
| Glass Transition Temperature | 150 | °C | ASTM D3418 |
| Peak Melting Temperature | 340 | °C | ASTM D3418 |
| CLTE - Flow (-50 to 50°C) | 1.7E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | DSC | ||
| 50°C | 1300 | J/kg/°C | |
| 200°C | 1730 | J/kg/°C | |
| Thermal Conductivity | 0.29 | W/m/K | ASTM E1530 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.9E+17 | ohms | ASTM D257 |
| Volume Resistivity | 1.9E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.44 | ||
| 1 kHz | 3.44 | ||
| 1 MHz | 3.41 | ||
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 1.0E-3 | ||
| 1 kHz | 1.0E-3 | ||
| 1 MHz | 3.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 20.3 mm | V-0 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C, 1000 sec^-1) | 850 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 365 | °C | |
| Middle Temperature | 370 | °C | |
| Front Temperature | 375 | °C | |
| Nozzle Temperature | 380 | °C | |
| Mold Temperature | 175 to 205 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 5" x 0.5" x 0.125" |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Type 1A, 5 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9451-90 Natural | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |
| Trexprene® A64NU | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| ALCOM® LD2 PC 1000 14008 WT1011-14 | ALBIS PLASTIC GmbH | PC | ALCOM® LD2 PC |
| MAXAMID™ PA6MG40-BK | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |
| LEXAN™ FXM121R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |