NORYL™ PKN4752F resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o0QW1N_NORYL-PKN4752F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPE+PS blend. High Heat. Translucent with yellow tint in natural color. FDA compliant. Extrusion and Injection Molding. Typical applications include High Performance Food Packaging, Electronics and Healthcare Packaging. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.90 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3010 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 86.2 | MPa | ASTM D638 |
| Fracture | 73.8 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 6.0 | % | ASTM D638 |
| Fracture | 15 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 50.0mm span 4 | 3150 | MPa | ASTM D790 |
| 100mm span 5 | 2950 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| Yield, 50.0mm span 6 | 145 | MPa | ASTM D790 |
| Yield, 100mm span 7 | 137 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 6.55 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 161 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 151 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 152 | °C | ASTM D648 |
| Vicat Softening Temperature | 174 | °C | ASTM D1525 8 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 6.3E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 5.6E-5 | cm/cm/°C | ASTM E831 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 2.0E-4 | % | |
| Cylinder Zone 1 Temp. | 204 - 227 | °C | |
| Cylinder Zone 2 Temp. | 216 - 238 | °C | |
| Cylinder Zone 3 Temp. | 238 - 266 | °C | |
| Cylinder Zone 4 Temp. | 238 - 266 | °C | |
| Adapter Temperature | 238 - 266 | °C | |
| Melt Temperature | 266 - 277 | °C | |
| Die Temperature | 238 - 266 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 8 hrsRoll Stack Temp - Bottom: 104 - 121 °CRoll Stack Temp - Middle: 104 - 121 °CRoll Stack Temp - Top: 104 - 121 °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.6 mm/min |
| 8 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) M/MI 40 K1836 | A. Schulman Europe | ABS | POLYMAN® |
| Baoding 67I85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Ebalta MG 707 / Z 400 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| Glastic® SLC-1000 | Bulk Molding Compounds, Inc. | Polyester, TS | Glastic® |
| INNOPOL® PP CS 2-9524 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |