Chemlon® 109-33 G
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o088il_Chemlon-109-33-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Chemlon® 109-33 G is a Polyamide 66 (Nylon 66) material filled with 33% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Chemlon® 109-33 G are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 145 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | |
| Break | 4.0 | % | |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 130 | J/m | |
| 23°C | 190 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 235 | °C | ASTM D648 |
| Melting Temperature | 257 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 11 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.749 mm) | HB | UL 94 | |
| Oxygen Index | 24 | % | ASTM D2863 |
| FMVSS Flammability | PASSES | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 241 to 257 | °C | |
| Middle Temperature | 257 to 271 | °C | |
| Front Temperature | 263 to 279 | °C | |
| Nozzle Temperature | 263 to 282 | °C | |
| Processing (Melt) Temp | 263 to 282 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 HV 11 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Verolloy B1500 | PlastxWorld Inc. | ABS+PBT | Verolloy |
| AKROMID® B3 GF 30 natural (2472) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Pearlthane® 11H98 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |
| Sylvin 2900-60 Clear Pink 6308 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |