Vi-Chem PVC V143-60I
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Vi-Chem Corporation |
| Trademark: | Vi-Chem PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nzYK0E_Vi-Chem-PVC-V143-60I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vi-Chem PVC V143-60I is a Polyvinyl Chloride material. It is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792A, ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec, 2.00 mm, Compression Molded) | 57 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield, 2.00 mm, Compression Molded | 8.50 | MPa | ISO 527-2/5 |
| 2.00 mm, Compression Molded 1 | 8.50 | MPa | ASTM D638 |
| Tensile Elongation (Break, 2.00 mm, Compression Molded) | 400 | % | ASTM D638, ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | |||
| 2.00 mm 2 | 26.9 | kN/m | ASTM D624 |
| 2.00 mm 3 | 27 | kN/m | ISO 34-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (85°C, 100 hr) | -1.3 | % | ASTM D573, ISO 188 |
| Change in Ultimate Elongation in Air (85°C, 100 hr) | 5.4 | % | ASTM D573, ISO 188 |
| Change in Mass in Air (85.0°C, 100 hr) | 1.0 | % | ASTM D573 |
| Change in Mass in Air (85.0°C, 100 hr) | 1.0 | % | ISO 188 |
| Thermal | Nominal Value | ||
|---|---|---|---|
| Cold Flexibility 4(-40°C) | No Cracks |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Florida Weathering - Delta E 5 | 1.98 | SAE J1976 | |
| Soiling 6 | Pass | ||
| Xenon Arc - Delta E 7 | 0.650 | SAE J1885 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 85 | mm/min | ISO 3795 |
| Note Message | |
|---|---|
| 1 . | Type IV, 500 mm/min |
| 2 . | Die C |
| 3 . | Method Ba, Angle (Unnicked) |
| 4 . | FLTM BN 102-01 |
| 5 . | 1 yr |
| 6 . | FLTM BN 112-08 |
| 7 . | 601.6 kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AGILITY™ 1001 Performance LDPE | The Dow Chemical Company | LDPE | AGILITY™ |
| BLUESTAR® 1100A | Nantong Xingchen Synthetic Material Co., Ltd. | PBT | BLUESTAR® |
| Kingfa FRHIPS-100 | Kingfa | PS (HIPS) | Kingfa |
| Hydrin® H65 | Zeon Chemicals L.P. | Epoxy | Hydrin® |
| Plaskon MUF-2C | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |