Ebalta GH 707 / BR
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nzLh0v_Ebalta-GH-707-BR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta GH 707/BR is a two components epoxy resin, which cures at room temperature. Due to very fine and hard fillers, this system gets a dense pressure resistant structure and hard wear resistant surface. Compared to foundry mould sand ebalta GH 707/BR shows a very good release properties and low tackiness casting thickness up to 30 mm. Applications
Properties
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 83 to 89 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 5100 to 5700 | MPa | ISO 178 |
| Flexural Stress | 70.0 to 80.0 | MPa | ISO 178 |
| Compressive Stress | 80.0 to 90.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 6.0 to 10 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Martens Temperature | 56 to 60 | °C | DIN 53458 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 14 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.95 to 2.05 | g/cm³ | |
| Viscosity (25°C) | 6.2 to 7.8 | Pa·s | |
| Curing Time (20°C) | 10 to 12 | hr | |
| Pot Life 1(20°C) | 35 to 45 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide PK005EI2 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| Westlake LDPE EF608 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| IDI STC 1023 | IDI Composites International | Polyester, TS | IDI STC |
| LNP™ THERMOCOMP™ Noryl_PX2926 compound | SABIC Innovative Plastics Europe | PPE+PS | LNP™ THERMOCOMP™ |
| PENTAMID A GV30 HYD2 black | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |