TAROMID A 280 H G6 DX0 TR1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nz4cgu_TAROMID-A-280-H-G6-DX0-TR1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66 medium viscosity 30% glass fibres reinforced, flame retardant UL94 V0, heat stabilized, very good flame proofing also at low thickness. High mechanical and thermal properties, low shrinkage and high dimensional stability, high tracking resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 - 1.58 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.45 - 0.75 | % | Internal method |
| Flow direction | 0.30 - 0.50 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.50 | % | ISO 62 |
| Saturated, 23°C | 4.5 | % | ISO 62 |
| Granule Humidity 1 | % |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reaction to Fire | I2 | NF F 16-101/102 | |
| Smoke Index | F3 | NF F 16-101/102 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(850°C) | 30 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 145 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 9200 | MPa | ISO 178 |
| Flexural Stress 4 | 206 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 32 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed) | 240 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 242 | °C | ISO 306/B50 |
| Ball Pressure Test (230°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 250 - 256 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 26 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.70 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| Comparative Tracking Index | IEC 60112 | ||
| Solution a | > 400 | V | IEC 60112 |
| Solution B | > 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 35 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 90.0 - 110 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 80 to 100°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1 hr |
| 3 . | 1.0 mm/min |
| 4 . | 1.0 mm/min |
| 5 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Rite® M690 | Lubrizol Advanced Materials, Inc. | PETG | Stat-Rite® |
| Zytel® RS LC4601 NC010 | DuPont Performance Polymers | Nylon, Unspecified | Zytel® RS |
| Mylar® EL (48 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| CoREZYN® COR31-DA-208 | Interplastic Corporation | Polyester, TS | CoREZYN® |
| Petrothene® GA501 | LyondellBasell Industries | LLDPE | Petrothene® |