Category: | PVC, Unspecified , Polyvinyl Chloride |
Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
Trademark: | Karina |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | nyrFq8_Karina-IVORY-PVC-COMPOUND--E-70900-35-1-E-AC.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
FLAME RETARDANT PVC COMPOUND CLASS 70C (PVC/A) RECOMMENDED FOR INSULATION OF ELECTRICAL WIRES AND CABLES (BWF). |
General Information | |
---|---|
Additive |
|
Features |
|
Uses |
|
Appearance |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity 1 | 1.46 to 1.50 | g/cm³ | ASTM D792 |
Color | 0.00OK | ME 12 | |
Color a | -2.62 to 3.38 | ME 12 | |
Color b | 2.51 to 8.51 | ME 12 | |
Color L | 85.8 to 91.8 | ME 12 |
Additional Information | Nominal Value | Unit | Test Method |
---|---|---|---|
Maximum Variation of Elongation | < 25 | % | IEC 60811-1-2 |
Maximum Variation of Tensile Strength | < 25 | % | IEC 60811-1-2 |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Durometer Hardness (Shore A, 15 sec) | 88 to 92 | ASTM D2240 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength | > 12.6 | MPa | ASTM D638 |
Tensile Elongation (Yield) | > 150 | % | ASTM D638 |
Elastomers | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength 2 | > 12.6 | MPa | IEC 60811-1-2 |
Tensile Elongation 3(Break) | > 150 | % | IEC 60811-1-2 |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Volume Resistivity 4 | > 3.0E+14 | ohms·cm | ASTM D257 |
Flammability | Nominal Value | Unit | Test Method |
---|---|---|---|
Oxygen Index | > 30 | % | NBR 6245 |
Note Message | |
---|---|
1 . | 24 hr |
2 . | Aged in Air for 168 hr at 100°C |
3 . | Aged in Air for 168 hr at 100°C |
4 . | 24 hr |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
SAXAMID™ 136Q32 | SAX Polymers | Nylon 6 | SAXAMID™ |
Vyncolit® 2530W | Vyncolit N.V. | Phenolic | Vyncolit® |
alphalon™ E 40 LN | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
Hax™ HF 417 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
Hostacom X M2 U36 | LyondellBasell Industries | PP Copolymer | Hostacom |