PRE-ELEC® PE 1291
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nyg8WK_PRE-ELEC-PE-1291.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PE 1291 is a conductive thermoplastic compound based on PE-HD. The electrical conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PE 1291 has an excellent balance of mechanical properties and is easy to extrude. Typical applications include blow moulded bottles, containers and canisters or mono- or co-extruded pipes and sheets. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/10.0 kg | 0.70 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 2.5 - 3.5 | % | ASTM D955 |
| Flow direction | 2.5 - 3.5 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 97 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Flow : Yield | 24.8 | MPa | ASTM D638 |
| Flow : Yield | 25.0 | MPa | ISO 527-2 |
| Flow | 26.2 | MPa | ASTM D638 |
| 0.400 mm 1 | 26.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Transverse flow : Yield | 9.0 | % | ISO 527-2 |
| Flow : Yield | 14 | % | ISO 527-2 |
| Fracture, 4.00mm 2 | > 500 | % | ISO 527-2 |
| Fracture, 4.00mm 3 | > 650 | % | ISO 527-2 |
| Flexural Modulus (4.00 mm) | 1200 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 4 | |||
| -20°C | 23 | kJ/m² | ASTM D256, ISO 179 |
| 23°C | 40 | kJ/m² | ISO 179, ASTM D256 |
| Charpy Unnotched Impact Strength 5 | |||
| -20°C | No Break | ASTM D256, ISO 179 | |
| 2°C | No Break | ISO 179 | |
| 23°C | No Break | ASTM D256 | |
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 21.0 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 44.1 | kJ/m² | ASTM D256 |
| Notched Izod Impact 6 | ISO 180 | ||
| -20°C | 20 | kJ/m² | ISO 180 |
| 23°C | 45 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ASTM D256 | |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength 7 | ISO 180 | ||
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 82.2 | °C | ASTM D648B |
| 0.45 MPa, not annealed | 82.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 47.8 | °C | ASTM D648A |
| 1.8 MPa, not annealed | 48.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 60.0 | °C | ASTM D1525, ISO 306/B50 6 8 |
| -- | 126 | °C | ASTM D1525, ISO 306/A50 7 9 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+5 | ohms | IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+4 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 2 Temp. | 210 | °C | |
| Cylinder Zone 3 Temp. | 220 | °C | |
| Cylinder Zone 4 Temp. | 220 | °C | |
| Cylinder Zone 5 Temp. | 230 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 230°C |
| Note Message | |
|---|---|
| 1 . | Flow |
| 2 . | Across Flow |
| 3 . | Flow |
| 4 . | 4 mm thickness |
| 5 . | 4 mm thickness |
| 6 . | 4 mm thick |
| 7 . | 4 mm thickness |
| 8 . | 标准 B (120°C/h), 载荷2 (50N) |
| 9 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-4000-GF30 | QTR, Inc. | PPE+PS+Nylon | QR Resin |
| Tecnoprene® A60K6 NAT001 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| Sumikon® FM-MK115S | Sumitomo Bakelite Co., Ltd. | PPS | Sumikon® |
| 3M™ Dyneon™ PTFE TF 2073Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| TECHNYL STAR® S 60G1 V30 GREY R7012 | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |