Order Products : sales@su-jiao.com
Petrotene® PP A3 G30 DOR0078 PH328 MSP
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nyb8aY_Petrotene-PP-A3-G30-DOR0078-PH328-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrotene® PP A3 G30 DOR0078 PH328 MSP is a Polypropylene material filled with 25% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Petrotene® PP A3 G30 DOR0078 PH328 MSP: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 to 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 3.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 1.0 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.0 to 2.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3000 | MPa | ASTM D790 |
| Flexural Strength | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 100 | °C | ASTM D648 |
| Vicat Softening Temperature | 120 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 40 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 1.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Operating Temperature | 100 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyre-ML® RC-5069 | Industrial Summit Technology Co. | API | Pyre-ML® |
| BJB Polyurethane F-64 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Geon™ Vinyl Rigid Extrusion 87345 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Plaslube® POM CO GM30 TL5 | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |
| Sumikon® PM-6280 | SBHPP | Phenolic | Sumikon® |