Sarlink® TPV X5750DB
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nxSw6G_Sarlink-TPV-X5750DB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink® TPV X5750DB is a Thermoplastic Vulcanizate (TPV) material. It is available in Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.958 | g/cm³ | ASTM D792 |
| -- | 0.960 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore D, 5 sec, Extruded | 49 | ||
| Shore D, 5 sec, Injection Molded | 52 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| Across Flow : 100% Strain | 13.1 | MPa | |
| Flow : 100% Strain | 18.0 | MPa | |
| Tensile Strength | ASTM D412, ISO 37 | ||
| Across Flow : Break | 23.0 | MPa | |
| Flow : Break | 21.5 | MPa | |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Across Flow : Break | 640 | % | |
| Flow : Break | 490 | % | |
| Tear Strength - Across Flow | |||
| -- | 142 | kN/m | ASTM D624 |
| -- 1 | 140 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 55 | % | |
| 70°C, 22 hr | 67 | % | |
| 125°C, 70 hr | 85 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | |||
| 135°C, 1000 hr | -20 | % | ASTM D573, ISO 188 |
| 100% Strain, 135°C, 1000 hr | 24 | % | ASTM D573 |
| 150°C, 168 hr | -16 | % | ASTM D573, ISO 188 |
| 100% Strain, 150°C, 168 hr | 15 | % | ASTM D573 |
| 100% Strain 135°C, 1000 hr | 24 | % | ISO 188 |
| 100% Strain 150°C, 168 hr | 15 | % | ISO 188 |
| Change in Ultimate Elongation in Air - Across Flow | ASTM D573, ISO 188 | ||
| 135°C, 1000 hr | -30 | % | |
| 150°C, 168 hr | -25 | % | |
| Change in Durometer Hardness in Air | ASTM D573, ISO 188 | ||
| Shore D, 135°C, 1000 hr | 4.0 | ||
| Shore D, 150°C, 168 hr | 3.0 | ||
| Change in Volume (125°C, 70 hr, in IRM 903 Oil) | 38 | % | ASTM D471, ISO 1817 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary @ 206/s | |||
| 200°C | 430 | Pa·s | ISO 11443 |
| 200°C | 430 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Queo™ 0230 | Borealis AG | Plastomer | Queo™ |
| SCANAMID 66 A11^ X30 LS | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Nylene® 132 HSL | Custom Resins Group | Nylon 66 | Nylene® |
| DAPCO™ 3008 | Cytec Industries Inc. | Epoxy | DAPCO™ |
| ESPRENE EPDM 601F | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |