SLOVAMID® 6 GF 15 T 25 TS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nwor5M_SLOVAMID-6-GF-15-T-25-TS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Good anisotropy of the manufacturing shrinkage. The talc is added to get the material shrinkage identical in both directions. Application for flat products in disc form /no screw after cooling off/ and for thick-walled products, at which the protection against the material failure is guaranteed. Delivered in natural mode and in the full RAL colour scale. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 0.71 | % | |
| Flow | 0.64 | % | |
| Water Content | 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 120 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 7300 | MPa | ISO 178 |
| Flexural Stress | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 45 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 200 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 200 | °C | ISO 306/B |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN® T2000HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Adell Polyamide AW-77 | Adell Plastics, Inc. | Nylon 66/6 | Adell Polyamide |
| Diamond GPPS GP-525 | Diamond Polystyrene | PS (GPPS) | Diamond GPPS |
| HiFill® PA6/6 GF70 HS L BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| ADENE® M38VQEGD00 | A.D. Compound S.p.A. | PP Copolymer | ADENE® |