POLYLAC® PA-777B
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYLAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nvxBZL_POLYLAC-PA-777B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYLAC® PA-777B is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. Characteristics include:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 7.5 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 7.50 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 | |
| Ball Indentation Hardness (H 358/30) | 91.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 45.0 | MPa | ISO 527-2/50 |
| Break | 34.0 | MPa | ISO 527-2/50 |
| 3.00 mm 1 | 42.7 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break, 3.00 mm 2 | 15 | % | ASTM D638 |
| Break | 18 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 6.00 mm 3 | 2160 | MPa | ASTM D790 |
| -- 4 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.00 mm 5 | 63.7 | MPa | ASTM D790 |
| -- 6 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 20 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C, 3.00 mm | 230 | J/m | ASTM D256 |
| 23°C, 6.00 mm | 200 | J/m | ASTM D256 |
| -- | 19 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 97.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 107 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 115 | °C | ASTM D1525 7 |
| -- | 113 | °C | ISO 306/A50 |
| -- | 105 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 95.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Mold Temperature | 30.0 to 70.0 | °C | |
| Injection Pressure | 4.90 to 6.86 | MPa | |
| Holding Pressure | 3.92 to 5.88 | MPa | |
| Back Pressure | 0.490 to 1.47 | MPa |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 6060 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Supol H-622 | Shanghai Suptech Engineering Plastics Co. Ltd. | TPO (POE) | Supol |
| AKROTEK® PEEK CF 40 9 black (5182) | AKRO-PLASTIC GmbH | PEEK | AKROTEK® |
| Hytrel® G4074 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Karina IVORY PVC COMPOUND 858-35/1-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |