LNP™ THERMOCOMP™ 5C004 compound
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nv4OLs_LNPTHERMOCOMP5C004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 5C004 is a compound based on Polyvinylidene Fluoride resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound FP-VC-1004 Product reorder name: 5C004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 16400 | MPa | ASTM D638 |
| Tensile Strength (Break) | 84.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.70 | % | ASTM D638 |
| Flexural Modulus | 13900 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 290 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 154 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NatureFlex™ NP 80 | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| ANYPOL CL-200LL | SH Energy & Chemical | PS (EPS) | ANYPOL |
| Geon™ Vinyl Fittings 87431 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Fittings |
| MAJORIS PBT 9237 3030 FB BLACK 8229 | AD majoris | PBT | MAJORIS |
| Sylvin 8600-64D Grey 9456 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |