Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. Glass reinforced nylon 6 materials offer significant improvements in strength, moduli, and deflection temperature over the base resin. They usually display improved moldability over glass reinforced nylon 6/6 materials with slight decreases in properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.95 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13800 | MPa | ASTM D638 |
| Tensile Strength | 207 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 12400 | MPa | ASTM D790 |
| Flexural Strength | 228 | MPa | ASTM D790 |
| Compressive Strength | 165 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 180 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.35 mm) | 1300 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 216 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 210 | °C | ASTM D648 |
| CLTE - Flow | 1.8E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.52 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.014 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 3mil/in.Flammability, ASTM D-635: B in/min. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 232 - 260 | °C | |
| Middle Temperature | 232 - 260 | °C | |
| Front Temperature | 232 - 260 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC A3 G30 HUV NTL0001 PC308 | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| RheTech Thermoplastic Polyolefin FT4200-01 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Royalite R922 | Spartech Plastics | PC+ABS | Royalite |
| Niuk 20NT02 | Shanghai Niuk New Plastic Technology Co., Ltd. | ABS | Niuk |
| Fixmaster Deep Pour Grout | Loctite® | Epoxy | Fixmaster |