Daelim Po1y® XP9100
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | DAELIM INDUSTRIAL CO., LTD. |
| Trademark: | Daelim Po1y® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nuhx6l_DaelimPo1yXP9100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daelim Po1y®XP9100 is a metallocene linear low density polyethylene product,. It is available in Europe or Asia Pacific. Daelim Po1y®XP9100 applications include bags/linings, wrappers, movies and food contact applications. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 56.9 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 52.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 630 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 650 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 300 | g | ASTM D1709A |
| Seal Initiation Temperature 1(50 µm, Blown Film) | 118 | °C | Internal method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ASTM D1004 | ||
| Lateral flow : 0.0500mm | 142 | kN/m | ASTM D1004 |
| Traffic : 0.0500mm | 137 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 117 | °C | ASTM D1525 |
| Peak Melting Temperature | 119 | °C | ASTM D3418 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 85 | ASTM D2457 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 200 | °C |
| Note Message | |
|---|---|
| 1 . | HGT, 2.8 kg, 0.5 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF5CGT (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Europrene® SOL TH 2314 | Versalis S.p.A. | SEBS | Europrene® |
| KOPELEN B-320 | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| INELEC PA6CF10 | Infinity LTL Engineered Compounds | Nylon 6 | INELEC |
| SABIC® HDPE CC453G | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |