Lumiloy® GP1000D
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nu6B5A_Lumiloy-GP1000D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding Grade, General Purpose Description High Impact Strength Application Electric and Electronic Parts |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 7.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 57.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 40 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2280 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 3.20 mm) | 96.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 128 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 134 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | > 0.030 | % | |
| Rear Temperature | 260 to 300 | °C | |
| Middle Temperature | 270 to 310 | °C | |
| Front Temperature | 270 to 310 | °C | |
| Nozzle Temperature | 270 to 310 | °C | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 70.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer SV-56000U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| WPP PP UP4G402-Natural/PPH2LTF4-Natural | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| SABIC® FORTIFY™ C3070D | Saudi Basic Industries Corporation (SABIC) | TPO (POE) | SABIC® FORTIFY™ |
| Vyncolit® TX10916/5 | SBHPP | Phenolic | Vyncolit® |
| DAI-EL™ G-621 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |