Chemlon® 130 G
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ntQ5TT_Chemlon-130-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Chemlon® 130 G is a Polyamide 66 (Nylon 66) material filled with glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Chemlon® 130 G: Flame Rated. Typical application of Chemlon® 130 G: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.15 to 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.90 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 165 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | |
| Break | 3.0 | % | |
| Flexural Modulus | 8100 | MPa | ASTM D790 |
| Flexural Strength | 252 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 240 | °C | ASTM D648 |
| Melting Temperature | 257 | °C | |
| CLTE - Flow | 3.1E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 16 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.749 mm) | HB | UL 94 | |
| Oxygen Index | 25 | % | ASTM D2863 |
| FMVSS Flammability | PASSED |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 241 to 257 | °C | |
| Middle Temperature | 257 to 271 | °C | |
| Front Temperature | 263 to 280 | °C | |
| Nozzle Temperature | 263 to 282 | °C | |
| Processing (Melt) Temp | 263 to 282 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDILENE H 490 M40 F | ADDIPLAST | PP, Unspecified | ADDILENE |
| Hostacom 65F4-4C | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Hytrel® PC948 NC010 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Iupiace® GN20 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| PERLAS® O07F3000B01 | A.D. Compound S.p.A. | PP Homopolymer | PERLAS® |