DOW™ LDPE 4010
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ntNbAO_DOW-LDPE-4010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dow Polyethylene LDPE 4010 is a general purpose Extrusion Coating Resin. It complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 8.00 | MPa | ISO 527-2 |
| -- | 12.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 500 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 89.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 105 | °C | Internal method |
| Additional Information |
|---|
| Selection note: WVTR: Lyssy or Mocon Chill roll: matte or glossy Air gap:250mm or 200mm Nip Off-set : -15mm or 0mm Tset: 260, 290 or 320°C Substrate: Paper type (e.g. Kraft Paper) or Film type (OPP) - weight in g/m² or thickness in micron |
| Extrusion | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Neck-in 1(290°C) | 100.0 | mm | Internal method |
| Drop down 2(290°C) | 230 | m/min | Internal method |
| Minimum coating weight- Calculated 3(290°C) | 7.0 | g/m² | Internal method |
| Extrusion instructions |
|---|
| Fabrication Conditions for Extrusion Coatings: Laminator settings applied for extrusion processing: Air-gap = 250 mm Nip-off set = -15 mm Chill Roll glossy |
| Note Message | |
|---|---|
| 1 . | 25g/m² coatings at selected running conditions |
| 2 . | Acceleration from 15g/m² coating at selected set extruder temperature |
| 3 . | Acceleration from 15g/m² coating at selected setextruder temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 AR 10 TFE 10 | RTP Company | Acetal (POM) Copolymer | RTP |
| Trithene® TS 8090 | Petroquimica Triunfo | LDPE | Trithene® |
| Ferro PP TPP30AN60GY | Ferro Corporation | PP, Unspecified | Ferro PP |
| Fainplast PVC RK 320 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| LNP™ THERMOCOMP™ AX04518 compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |