NYLAFORCE® B 50
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LEIS Polytechnik - polymere Werkstoffe GmbH |
| Trademark: | NYLAFORCE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nsiCYg_NYLAFORCE-B-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| produced by feed up-process, polyamide 6 + 50% glass fibres, heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.10 to 0.50 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C 2 | -- | 12000 | MPa | |
| 23°C | 17500 | -- | MPa | |
| 80°C | 7600 | -- | MPa | |
| 120°C | 7400 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| 23°C 3 | -- | 170 | MPa | |
| 23°C | 250 | -- | MPa | |
| 80°C | 140 | -- | MPa | |
| 120°C | 105 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, 23°C 4 | -- | 5.5 | % | |
| Break, 23°C | 3.2 | -- | % | |
| Break, 80°C | 7.4 | -- | % | |
| Break, 120°C | 7.6 | -- | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -- | 19 | -- | kJ/m² | |
| 23°C 5 | -- | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -- | 100 | -- | kJ/m² | |
| 23°C 6 | -- | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 7 | 221 | -- | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | 60 mm x 60 mm x 2 mm |
| 2 . | Tested according to ISO 527/ISO 1110 |
| 3 . | Tested according to ISO 527/ISO 1110 |
| 4 . | Tested according to ISO 527/ISO 1110 |
| 5 . | Tested according to ISO 179/ISO 1110 |
| 6 . | Tested according to ISO 179/ISO 1110 |
| 7 . | 10K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOPAS® 6013S-04 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| TRILAC® ABS-RC3000 | Polymer Technology and Services, LLC | ABS | TRILAC® |
| Witcom PPS 8G/3L1 | Witcom Engineering Plastics B.V. | PPS, Branched | Witcom PPS |
| Evoprene™ 049 | AlphaGary | SBS | Evoprene™ |
| Karina IVORY TR (SP31503) -E TR-600N35/ 1-YT-A | Karina Ind. e Com. de Plásticos Ltda | TPE | Karina |