Polymer-E C4100
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Asia Polymer Corporation (APC) |
| Trademark: | Polymer-E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nsGs1k_Polymer-E-C4100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polymer-E C4100 is a Low Density Polyethylene product. It can be processed by extrusion and is available in Asia Pacific. Applications of Polymer-E C4100 include coating applications and film. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.8 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 11.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 450 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 54.0 | °C | ASTM D648 |
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 73 | ASTM D2457 | |
| Haze | 6.3 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 GB 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| Shin-Etsu Elastomer FE-381U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| TECHNYL® A 218 V25 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Starex SP-0183 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| PHOENIX™ 9451 | Phon Tech Industrial Company | TPE | PHOENIX™ |