BJB Polyurethane TC-854 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nrBqBR_BJB-Polyurethane-TC-854-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TC-854 A/B is a rigid 84 Shore D polyurethane system that exhibits exceptional physical properties. It is a high performance material that features high heat deflection capability and a low shrink factor. TC-854 is a highly translucent, colorless casting material that allows for unrestricted tinting and precise color matching. This product is ideal for producing intrinsically colored parts requiring a non-painted finish. This product can be easily processed for hand-cast, meter-mix- dispense, or vacuum cast applications. Product Highlights:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Specific Gravity | |||
| Part A : 25°C | 1.167 | g/cm³ | |
| Part B : 25°C | 1.067 | g/cm³ | |
| Shrinkage 1 | 0.10 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Gel Time | 7.0 - 9.0 | min | |
| Work Time (25°C) 2 | 6.0 - 8.0 | min |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Brokfield Viscosity | |||
| Mixed : 25°C | 450 | mPa·s | |
| Part A : 25°C | 165 | mPa·s | |
| Part B : 25°C | 725 | mPa·s |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure Time (25°C) | 5.0 - 7.0 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 82 - 86 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2280 | MPa | ASTM D638 |
| Tensile Strength | 69.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 11 | % | ASTM D638 |
| Flexural Modulus | 2480 | MPa | ASTM D790 |
| Flexural Strength | 94.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 61 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 85.0 - 90.6 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 73.9 - 79.4 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Component B | Mixing ratio by weight: 60, mixing ratio by capacity: 66 | ||
| Shelf Life | 26 | wk | |
| Demold Time (25°C) | 120 - 180 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Note: Reported physical properties based on elevated temperature cured test specimens.In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77° (25°C), followed by 16 hours at 150-180°F (66-82°C). Support of the part may be required to prevent part deformation during heat cure. |
| Note Message | |
|---|---|
| 1 . | 12" x 1/2" x 1/2" |
| 2 . | 100g mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene TPP1010 | Teknor Apex Asia Pacific PTE. LTD. | PP Homopolymer | Sinpolene |
| Zhongfa PP pp8 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Buna® EP G 2470 LM | LANXESS Corporation | EPDM | Buna® EP |
| Geon™ Vinyl Flexible R3792C | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Petrotene® PP A3 G20 NTLA010 PH304 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |