TECACOMP® PET TRM black 9415
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nqXqlr_TECACOMPPETTRMblack9415.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | |
| Apparent Density | 0.67 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 85 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.79 | % | ISO 294-4 |
| Flow | 0.24 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14500 | MPa | ISO 527-2/50 |
| Tensile Stress | 175 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 235 | °C | ISO 75-2/A |
| Glass Transition Temperature | 70.0 | °C | DIN 53765 |
| Melting Temperature | 255 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 80 to 110°C | 8.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 80 to 110°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 0.40 | W/m/K | DIN EN 821 |
| -- 2 | 1.4 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 110 | °C | |
| short term | 170 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.3E+5 | ohms·cm | ISO 3915 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 120 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 130 - 160 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 382 TFE 15 | RTP Company | PC | RTP |
| APEX® RE 8222 | Teknor Apex Company | PVC, Rigid | APEX® |
| DJSilicone NE--T-2/NE-T-2U (standard) | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Karina GRAY PVC COMPOUND 701-DA-18/291-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PERSTIR® N10K7000AH0 | A.D. Compound S.p.A. | PS (GPPS) | PERSTIR® |