INSULCAST® RTVS 3-95-1
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® RTVS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nqWF27_INSULCAST-RTVS-3-95-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST RTVS 3-95-1 is a low viscosity, thermally conductive RTV silicone compound, UL recognized under file E86165 for flame class 94V-0. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 65 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 3.28 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 45 | % | ASTM D412 |
| Tear Strength 1 | 2.63 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 1.8E-4 | cm/cm/°C | |
| Thermal Conductivity | 1.4 | W/m/K | |
| Service Temperature | -55 to 260 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 5.00 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 5.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 5.0 | ||
| Shelf Life (25°C) | 26 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 2 | Clear/Transparent | ||
| -- 3 | Red | ||
| Density | |||
| -- 4 | 0.958 | g/cm³ | |
| -- 5 | 2.34 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| 25°C 6 | 1.0 | Pa·s | |
| -- 7 | 10 | Pa·s | |
| 25°C 8 | 15 | Pa·s | |
| Curing Time | |||
| 125°C | 0.25 | hr | |
| 90°C | 1.0 | hr | |
| 50°C | 4.0 | hr | |
| 25°C | 24 | hr | |
| Pot Life 9(25°C) | 90 | min |
| Note Message | |
|---|---|
| 1 . | Die B |
| 2 . | Part B |
| 3 . | Part A |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | Part B |
| 7 . | Mixed |
| 8 . | Part A |
| 9 . | 100 gram mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBESTA P3012 U | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| 3M™ Dyneon™ Fluoroplastic THV 610GZ | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroplastic |
| FHR EPS 40-3640 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| KOCETAL® GF702BK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| LEXAN™ EXL1444 resin | SABIC Innovative Plastics | PC | LEXAN™ |