Integra™ POK 9030 GA6
| Category: | PK , Polyketone |
| Manufacturer: | PolySource, LLC |
| Trademark: | Integra™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nq83Dg_IntegraPOK9030GA6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aliphatic Polyketone, Medium viscosity grade for injection molding, 30% Glass fiber reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 - 0.80 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50%RH) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 128 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | > 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 6850 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 141 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 205 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 500 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6105 BR | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Nylex鈩?1429 | Multibase, A Dow Corning Company | Nylon+PP | Nylex™ |
| DAI-EL™ G-763F | Daikin Fluorochemicals (China) Co., Ltd. | Fluorelastomer | DAI-EL™ |
| Polifil® PP RMT-20 | The Plastics Group | PP Impact Copolymer | Polifil® PP |
| Sylvin 83040-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |