Order Products : sales@su-jiao.com
LUVOCOM® 70-9113/BK
| Category: | PK , Polyketone |
| Manufacturer: | LEHVOSS Group |
| Trademark: | LUVOCOM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | npVYMN_LUVOCOM709113BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LUVOCOM®70-9113/BK is a Polyketone (PK) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 70-9113/BK are:
LUVOCOM®The typical application fields of 70-9113/BK are: engineering/industrial accessories |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 1.6 - 2.2 | % | DIN 16901 |
| Water Absorption (23°C, 24 hr) | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 57.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 18 | % | ISO 527-2 |
| Flexural Modulus | 1500 | MPa | ISO 178 |
| Flexural Stress | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 82 | kJ/m² | ISO 179/1fU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Continuous Use Temperature | 90.0 | °C | UL 746B |
| Maximum operating temperature- Short Term | 120 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation Resistance | > 1.0E+12 | ohms | IEC 60167 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 200 | °C | ISO 306/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Hot air dryer | 120 | °C | |
| Hot air dryer, B | 80 | °C | |
| Drying Time | |||
| Hot air dryer | 1.0 - 4.0 | hr | |
| Hot air dryer, B | 2.0 - 6.0 | hr | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 230 - 260 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 250 - 265 | °C | |
| Processing (Melt) Temp | 245 | °C | |
| Mold Temperature | 60 - 100 | °C |
| Injection instructions |
|---|
| General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE FI1157 | Saudi Basic Industries Corporation (SABIC) | HDPE, HMW | SABIC® HDPE |
| BLUESTAR® PBT 403M-G20 | Nantong Zhonglan Engineering Plastics Co., Ltd. | PBT | BLUESTAR® |
| Hanwha Total PP FB33 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| LAPEROS® S471 | Polyplastics Co., Ltd. | LCP | LAPEROS® |
| INLUBE PA612GF30TF13SI2 | Infinity LTL Engineered Compounds | Nylon 6/12 | INLUBE |