Kepex® 3330GB
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nor2Ak_Kepex3330GB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| shrinkage- Flow (3.00 mm) | 0.40 - 0.80 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 57.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 4300 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.3 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 22 | kV/mm | IEC 60243-1 |
| Dielectric Constant (60 Hz) | 3.40 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Hopper Temperature | 60 - 80 | °C | |
| Rear Temperature | 230 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 250 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 70 - 90 | °C | |
| Back Pressure | 0.490 - 0.981 | MPa | |
| Screw Speed | 80 - 120 | rpm |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE B5260LS | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| SCANBLEND FS8 ASUV4 | Polykemi AB | ASA+PC | SCANBLEND |
| Starflam RF0055E | Eurostar Engineering Plastics | Nylon 66/6 | Starflam |
| AMPLIFY™ TY 1052H | The Dow Chemical Company | MAH-g | AMPLIFY™ TY |
| Panlite® LN-2250Z | TEIJIN LIMITED | PC | Panlite® |