Rilsan® BMVO TLD
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | noaKOM_Rilsan-BMVO-TLD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® BMVO TLD is a polyamide 11 produced from a renewable source. This natural grade is designed for injection molding. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 30°C, 24 hr, 2.00 mm | 1.0 | % | |
| Flow : 30°C, 24 hr, 2.00 mm | 0.10 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 78 | ||
| Shore D, 15 sec | 71 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1370 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 42.0 | MPa | |
| Break | 56.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 1150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 189 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11, MHLR, 18-010 | ISO 1874 | |
| Renewable Carbon Conent | > 99 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 230 to 270 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX 10 G10 | Taro Plast S.p.A. | PBT | TAROLOX |
| NYCOA Polyamide 534 H | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Hostacom X M3 T16 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Hyundai EP PA6 LS405 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| Delas 185 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PVC+NBR | Delas |